(Summary description)Customized SILICONE STRUCTURAL SEALANT from China manufacturer refers to the adhesive with high strength, can bear large load, aging resistance, fatigue resistance and corrosion resistance, and has stable performance within the expected life. It is suitable for bearing the bonding of strong structural parts. Non structural adhesive has low strength and poor durability. It can only be used for bonding, sealing and fixing of ordinary and temporary properties, and cannot be used for structural adhesive bonding. NEUTRAL SILICONE WETHERPROOF SEALANT from China manufacturer is a structural adhesive with waterproof function. Silicone glue refers to the adhesive based on silicone rubber. According to different functions, it can be divided into structural adhesive, potting adhesive, sealant, thermal conductive adhesive, flame retardant adhesive and so on.
混煉膠硫化丁基防水嵌縫膠性能測試
(Summary description)Customized SILICONE STRUCTURAL SEALANT from China manufacturer refers to the adhesive with high strength, can bear large load, aging resistance, fatigue resistance and corrosion resistance, and has stable performance within the expected life. It is suitable for bearing the bonding of strong structural parts. Non structural adhesive has low strength and poor durability. It can only be used for bonding, sealing and fixing of ordinary and temporary properties, and cannot be used for structural adhesive bonding. NEUTRAL SILICONE WETHERPROOF SEALANT from China manufacturer is a structural adhesive with waterproof function. Silicone glue refers to the adhesive based on silicone rubber. According to different functions, it can be divided into structural adhesive, potting adhesive, sealant, thermal conductive adhesive, flame retardant adhesive and so on.
- 發布時間 : 2023-3-8 12:16:27
- Views:
Information
兩種方法的對比以及工業化生產的設想高溫法費時費力，排膠不暢，丁基防水嵌縫膠膠料極易殘留在開口反應器或密煉機上，耗時較長，而且此時PIB2300粘度較小，極易發生打滑，混合效果欠佳，每次排膠還需混合設備與丁基防水嵌縫膠膠料冷卻之后才能手動清除，制備工藝繁瑣，且與硫化體系的混合效果不理想，微交聯結構不均勻。
而低溫狀態下，由于剪切力較大，通過分批加入軟化劑PIB2300反而能后獲得較好的混合效果，排膠相對容易，且不會造成丁基防水嵌縫膠膠料提前硫化。以開煉機混合，雖然均勻度效果好，混合速度快，不易殘留，但是難以操作。若低溫下以密煉機混煉，同樣需要多次分段加入PIB2300。權衡之下，為了保證混合質量與實驗進度，本文獲取實驗數據的試樣皆采用低溫法開煉機混煉。
在實際生產中，可用高剪切的雙螺桿擠出機進行連續化涂敷生產，示意圖如圖2-2所示，將小料與基體混合均勻后，將丁基防水嵌縫膠膠料切成小粒，在擠出機中混合并輸送，可在螺桿的中央多設置幾個加入PIB2300的料斗，從而使PIB分段加入，后經過升溫，通過口模擠出到輪胎內側，通過擠出速度和輪胎轉速以及口模與輪胎間的距離可調節膠層厚度，另一種設想，便是直接用卷材的加工方式，將丁基防水嵌縫膠膠料做成泡棉膠一樣的卷材，然后烘烤熱處理，使用時，直接像雙面膠一樣貼在輪胎內側，這樣能夠更加方便地進行安全輪胎的生產。丁基防水嵌縫膠性能測試與表征。
根據國家標準GB/T9869-1997，用高無轉子硫化儀MV 3000VS高鐵儀器設備有限公司測試混煉膠的硫化特性。稱取Sg樣品，由于本文所制備的混煉膠模量極小，具有流動性，故形狀任意。樣品兩側應用薄玻璃紙包覆以防流動性過強的混煉膠在測試過程中滲入轉軸。
使用RZ平板流變儀，轉子與底板設距離為lmm，設置測試溫度為120℃,剪切速率范圍為0.011 OS單方向旋轉模式，用此方法測試混煉膠。平板流變儀主要表征此混煉膠在擠出涂布過程中的粘度。www.pegeankoch.com